Lithium Cobalt Oxide (LiCoO₂, LCO) Cathode Sheet – Single-Side Coated on Aluminum Foil (241 × 200 mm), 5 Sheets/Bag

This product is a single-side coated cathode sheet based on lithium cobalt oxide (LiCoO₂) deposited on aluminum current collector foil.

It is intended for laboratory-scale Li-ion cell fabrication and electrochemical performance evaluation.

The electrode is supplied in flat sheet format with defined coating area and controlled mass loading, suitable for coin cell or pouch cell assembly.

Each package contains 5 sheets.

Worldwide shipping

Shipping costs and lead time confirmed with your quotation.

Secure payment

Card payment and purchase orders accepted.

Technical support

Configuration and compatibility support from our engineers.

This combination does not exist.

Specification
Cathode Material	Lithium Cobalt Oxide (LiCoO₂, LCO)
Current Collector	Aluminum foil
Active Material Content	96 wt%
Sheet Size	241 mm (L) × 200 mm (W)
Effective Coated Area	241 mm × 175 mm
Uncoated Edge Width	12.5 mm per side
Aluminum Foil Thickness	16 µm
Coating Configuration	Single-side coated
Single-Side Areal Loading	11.5 ± 0.2 mg/cm²
Compaction Density	3.5 ± 0.1 g/cm³
Coating Thickness	~33 µm
Total Electrode Thickness	~50 µm
Specific Capacity	180 mAh/g (0.1C)
Quantity	5 sheets per bag

Pre-treatment Recommendation:
Dry the electrode sheets in a vacuum oven at 80–120 °C for 6–12 hours prior to use.
Storage Condition:
After opening, store in a dry atmosphere (preferably glovebox or desiccator) to prevent moisture absorption.